Spherical Alumina
Spherical alumina is produced by high-temperature melting, high spherical rates, high alphaphase aluminum oxide content. This product has superior performance in rubber, plastic, and ceramic feedstock.
Here is a summary of the methods for preparing spherical-grade alumina. Each method has its own characteristics.
Here are seven ways to prepare spherical aluminum:
1. Various sedimentation method
The precipitation process in homogeneous solutions is a crystal nuclear reaction. After that, the aggregation becomes greater and eventually from the solution from solution, it is usually unbalanced. But, if you lower the concentration of precipitant in homogeneous, even slowly Generation, then large numbers of microcrystals nuclei will be evenly produced. Finally, finely precipitated particle are uniformly dispersed throughout the entire solution, and a balance state is maintained over a longer period. Method for average prediction. Al2 (SO4)3, Al (NO3) 3 & urea are used as raw materials. Under the oil bath at 98 degrees C, the hydroxide produced by slow hydrolysis is precipitant. After calcination, the size and shape of the precursors can be adjusted by adjusting the proportion of SO422- with NO3-. Al2 (SO4) 3. The obtained colloid particles have a very good shape. This method was used in Al2(SO4) 3 and Urea as raw materials. The spherical (and hollow spherical) alumina powders were prepared under different conditions. A homogeneous precipitation process is possible if the precipitated particles obtained fall within the range for colloid particles. In addition to the conditions of SO42 – present, it is often difficult to finally form a glue of the globiosis in the gelation of sol particles to finally form a globiotype, so people think that this formation of sol-emulsion-condensation Gladle.
2. Sol-emulsion-gel method
This method is based on the sol-gel method. To obtain spherical powder particles from the oil phase, one uses the interface tension of both the oil and the water phases to form small spherical droplets. The aluminum hydrolysis process produced the spheroidized alu powder. In this case, 50% of the aluminum was removed, 40% of the acetonitrile and 9% of the dispersed water were retained. Using hydroxypropylcellulose as a dispersant to obtain a spherical g-alumina powder having a very good spherical degree.
3. Drip method
The droplet method is used for binding the alumina sol to the oil layer (usually using petroleum oil, mineral oil, or paraffin). The resulting spherical sol particle is then gelled in an alkaline ammonia solution. This method further enhances the sol-emulsion gel method.
4. Use templates
The template method controls the morphology during the production of spherical foodstock. The product is often hollow or has a nuclear-shell structure. The aluminum powder surface is used for simplifying the aluminum powder’s surface. While the template method can be used to prepare an air spherical ball sphere, it has limitations. The preparation steps are more involved and require more effort.
5. Gas solve decomposition method
The aerosol decomposition process is usually based upon an aluminum salt. It uses the properties of aluminum alcohol and high-temperaturepyrolysis to make aluminum salt. Next, it uses phase transition to alkoxide gasify, then contact with liquid water, then pick up high temperature or direct high temperatures, thereby achieving transitions of gas-liquid solid or gas-solid phase and finally, creating a spherical form of alumina powder. Complex experiments involving reaction moieties as well as atomizing moiety are key to this method.
6. Radio frequency induction plasma method
Radio frequency plasma treatment of alumina dust using radio frequency radiation. This plasma has high energy density and high heating power. It also allows for simple material processing. The powder is free from any electrodes and therefore not contaminated by electrode evaporation. It is possible for purity to be maintained. Additionally, irregularly shaped particles of alumina are sprayed into plasma torch with the feed gas. Plasma melts rapidly. Droplets will quickly solidify, creating spherical particle.
7. Jet
The essence and structure of spinal alumina are formed quickly by surface tension. You can divide it into spray heat, spray drying, and spray melting Law, depending on the characteristics of phase transformation. AlCl3, Al2 SO4) 3, Al (NO3) 3 solution form small droplets through atomization. The process also requires a high thermal decomposition temperature of around 900°C. The aluminum salt solution is first mixed with ammonia to form an alkali sol. After that, spray the alumina sol at between 150 and 240 C.
Tech Co., Ltd. () is a professional Spherical Alumina Over 12 years of chemical products research and product development experience. We accept credit cards, T/T and Paypal payments. We will ship goods overseas via FedEx, DHL and by air or sea to our customers.
1. Various sedimentation method
The precipitation process in homogeneous solutions is a crystal nuclear reaction. After that, the aggregation becomes greater and eventually from the solution from solution, it is usually unbalanced. But, if you lower the concentration of precipitant in homogeneous, even slowly Generation, then large numbers of microcrystals nuclei will be evenly produced. Finally, finely precipitated particle are uniformly dispersed throughout the entire solution, and a balance state is maintained over a longer period. Method for average prediction. Al2 (SO4)3, Al (NO3) 3 & urea are used as raw materials. Under the oil bath at 98 degrees C, the hydroxide produced by slow hydrolysis is precipitant. After calcination, the size and shape of the precursors can be adjusted by adjusting the proportion of SO422- with NO3-. Al2 (SO4) 3. The obtained colloid particles have a very good shape. This method was used in Al2(SO4) 3 and Urea as raw materials. The spherical (and hollow spherical) alumina powders were prepared under different conditions. A homogeneous precipitation process is possible if the precipitated particles obtained fall within the range for colloid particles. In addition to the conditions of SO42 – present, it is often difficult to finally form a glue of the globiosis in the gelation of sol particles to finally form a globiotype, so people think that this formation of sol-emulsion-condensation Gladle.
2. Sol-emulsion-gel method
This method is based on the sol-gel method. To obtain spherical powder particles from the oil phase, one uses the interface tension of both the oil and the water phases to form small spherical droplets. The aluminum hydrolysis process produced the spheroidized alu powder. In this case, 50% of the aluminum was removed, 40% of the acetonitrile and 9% of the dispersed water were retained. Using hydroxypropylcellulose as a dispersant to obtain a spherical g-alumina powder having a very good spherical degree.
3. Drip method
The droplet method is used for binding the alumina sol to the oil layer (usually using petroleum oil, mineral oil, or paraffin). The resulting spherical sol particle is then gelled in an alkaline ammonia solution. This method further enhances the sol-emulsion gel method.
4. Use templates
The template method controls the morphology during the production of spherical foodstock. The product is often hollow or has a nuclear-shell structure. The aluminum powder surface is used for simplifying the aluminum powder’s surface. While the template method can be used to prepare an air spherical ball sphere, it has limitations. The preparation steps are more involved and require more effort.
5. Gas solve decomposition method
The aerosol decomposition process is usually based upon an aluminum salt. It uses the properties of aluminum alcohol and high-temperaturepyrolysis to make aluminum salt. Next, it uses phase transition to alkoxide gasify, then contact with liquid water, then pick up high temperature or direct high temperatures, thereby achieving transitions of gas-liquid solid or gas-solid phase and finally, creating a spherical form of alumina powder. Complex experiments involving reaction moieties as well as atomizing moiety are key to this method.
6. Radio frequency induction plasma method
Radio frequency plasma treatment of alumina dust using radio frequency radiation. This plasma has high energy density and high heating power. It also allows for simple material processing. The powder is free from any electrodes and therefore not contaminated by electrode evaporation. It is possible for purity to be maintained. Additionally, irregularly shaped particles of alumina are sprayed into plasma torch with the feed gas. Plasma melts rapidly. Droplets will quickly solidify, creating spherical particle.
7. Jet
The essence and structure of spinal alumina are formed quickly by surface tension. You can divide it into spray heat, spray drying, and spray melting Law, depending on the characteristics of phase transformation. AlCl3, Al2 SO4) 3, Al (NO3) 3 solution form small droplets through atomization. The process also requires a high thermal decomposition temperature of around 900°C. The aluminum salt solution is first mixed with ammonia to form an alkali sol. After that, spray the alumina sol at between 150 and 240 C.
Tech Co., Ltd. () is a professional Spherical Alumina Over 12 years of chemical products research and product development experience. We accept credit cards, T/T and Paypal payments. We will ship goods overseas via FedEx, DHL and by air or sea to our customers.